DLP Materials

ROBUST MATERIALS & STRONG, END-USE PARTS

Our team at Seattle 3D Printing can create durable, high-detail end-use parts for any industry. With a wide selection of DLP materials, we can bring your designs to life.

Heat Resistant

LOCTITE 3D IND403

High-modulus, durable resin for enhanced temperature resistance.

Colors: Black
Ultimate Tensile Strength: 72 MPa
Elongation at Break: 10%
Tensile Modulus: 2572 MPa
HDT: 80°C

Ultracur3D RG 3280

Ceramic-filled resin with outstanding stiffness and excellent temperature resistance.

Colors: White
Ultimate Tensile Strength: 87 MPa
Elongation at Break: 1.3%
Tensile Modulus: 10600 MPa
HDT: 284°C

Tough

LOCTITE 3D 3172

Durable and impact-resistant, ideal for fixtures and tooling.

Colors: Grey
Ultimate Tensile Strength: 39 MPa
Elongation at Break: 105%
Tensile Modulus: 1494 MPa
HDT: 51°C

LOCTITE 3D 3843

High-impact, semi-flexible resin suitable for a broad range of applications.

Colors: Black, Matte Black, Clear
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 43%
Tensile Modulus: 1806 MPa
HDT: 60°C

Stratasys Dura56

Tough, impact-resistant photopolymer designed for functional applications where both aesthetics and durability are essential.

Colors: Black
Ultimate Tensile Strength: 44 MPa
Elongation at Break: 78%
Tensile Modulus: 1595 MPa
HDT: 52°C

General Purpose

Somos QuickGen500

Rapid-printing, adaptable resin for general and functional prototypes.

Colors: Clear
Ultimate Tensile Strength: 20 MPa
Elongation at Break: 42%
Tensile Modulus: 465 MPa
HDT: 62° C

Ultracur3D ST45

Reactive urethane polymer designed for high-performance functional components.

Colors: Black
Ultimate Tensile Strength: 53 MPa
Elongation at Break: 21%
Tensile Modulus: 2000 MPa
HDT: 63°C

Somos WeatherX 100

Environmentally resilient material engineered for end-use parts.

Colors: Black
Ultimate Tensile Strength: 60 ± 0.3 MPa
Elongation at Break: 26% ± 6.0
Tensile Modulus: 2128 ± 154 MPa
HDT: 67° C

Elastomers

LOCTITE 3D IND402

High-rebound elastomer with excellent resilience, perfect for lattice structures.

Colors: Black
Ultimate Tensile Strength: 5.5 MPa
Elongation at Break: 230%
Tensile Modulus: 42 MPa

Medical

LOCTITE 3D MED413

Biocompatible material designed for general medical applications.

Colors: White
Ultimate Tensile Strength: 46 MPa
Elongation at Break: 51%
Tensile Modulus: 1673 MPa
HDT: 68°C